Polypropylene sails

Discuss IOM design, building an IOM, information on suppliers, tuning an IOM, results of recent events, etc

Moderator: Pedro Egea

Post Reply
Jamestj
Posts: 63
Joined: 25 Aug 2004, 17:50
Location: Building one at the moment

Polypropylene sails

Post by Jamestj » 14 Mar 2005, 02:01

I have a roll of polypropylene plastic sheet bought from an office supplies shop. It is clear and shiney and about 10 microns thick.

Is polypropylene suitable for making IOM sails?

If I stick numbers on the sails they will show through mirror image. Is this acceptable?

The sails may be very difficult to see at a distance. Can this cause problems?

Is a glossy finish to sails as good as a mat finish?

Would transparent polypropylene be attacked by UV from the sun?

Whilst very strong in tension, a small nick causes it to tear quite easily. Is it strong enough?

Is this material available in different colours?

What is polypropylene sheet used for - has it got a more common name?


Thanks.

Arvin S.

Post by Arvin S. » 14 Mar 2005, 04:14

Whilst very strong in tension, a small nick causes it to tear quite easily. Is it strong enough?
That is probably why it is not used for RC sails. Actually in my opinion it should be easy for you to purchase mylar drafting film instead, it should be readily available plus you will be using "tested" sail material.

Remember in big fleet racing small nicks on your sails can easily happen when booms hit your sails in close encounters.

ptercinet
Posts: 6
Joined: 06 Jan 2004, 08:01
Location: FRA 672,673,747
Contact:

Post by ptercinet » 14 Mar 2005, 08:53

Hi,

I think that a polypropylen film is well too elastic, only a polyester film will give you a sufficient dimensional stability.
some germans skippers use crystal flower film with some success...
but I dont know wich type of material is it (PP,PE,PET).

Pierre
Pierre Fra 3632

User avatar
Olivier Cohen
IOMICA Chairman
Posts: 436
Joined: 02 Dec 2004, 17:11
Sail number: FRA 100
Design: Venti
Location: Nantes / France
France

Post by Olivier Cohen » 14 Mar 2005, 10:01

ptercinet wrote:Hi,

I think that a polypropylen film is well too elastic, only a polyester film will give you a sufficient dimensional stability.
some germans skippers use crystal flower film with some success...
but I dont know wich type of material is it (PP,PE,PET).

Pierre
Crystal flower film is made of PP.

I use it myself, and it is strong enough for A sails.
IOMICA Chairman

Jamestj
Posts: 63
Joined: 25 Aug 2004, 17:50
Location: Building one at the moment

Post by Jamestj » 19 Mar 2005, 01:09

Many help for the info.

Could anyone tell me where I could get some tiny grommets to put in the luf to prevent the material from tearing? I live in England so the company would have to do mail order.
I have tried melting holes in the material but it does not work too well.

Ralph Knowles
Posts: 35
Joined: 23 Nov 2003, 22:51
Location: Dundee, Scotland, GBR1876/ GBR 2182/GBR 2167/GBR 1907/GBR 3367
Contact:

Sail 'Grommets'

Post by Ralph Knowles » 19 Mar 2005, 05:10

Try www.sailsetc.com and click Products then Sails then Materials, and at item No 78 you will find 'Eyelets' and 'washers' at £1.50 or so per packet of 100 pieces. You will also have to buy a small punch and die to fix them. Find the phone number and give Lorna or Chris a call. They will gladly help I am sure. Send a stamped and addressed A5 envelope and they will forward a free catalogue by return.

Cheers

Ralph

Jamestj
Posts: 63
Joined: 25 Aug 2004, 17:50
Location: Building one at the moment

Post by Jamestj » 21 Mar 2005, 08:19

Thanks for that info, Ralph. Buying from a source specialising in IOM products means that they will be tried and tested in this application and won't rust or do other unpleasant things.

Can anyone help me with another problem I am having please?
I made a sail out of some drafting film. It looks OK until I try to make it take on the shape it would take if the wind was blowing from the opposite side. It sort of creases up and looks horible and obviously would not work if fitted on a boat.

I know that I am taking a liberty asking questions on this forum since I learnt elsewhere on this forum that it is suppose to be for members with boats already - so I guess some of the questions I have asked are rather dumb. However this is a schools project and it is best that I don't cheat and just copy other peoples ideas. However a sail if made concave it might 'snap' from one shape to another and this is clearly happening to my 'design'.

Obviously I have done something wrong. I thought that sails should have a double curvature, hence the need for seams. There is probably a very simple answer to my problem. Can anyone help please?